Thermoplastic spacer of MF910S hollow glass
The MF910S is a warm side spacing that produces hollow glass. The MF910S is composed of a thermoplastic elastomer containing a desiccant, and the desiccant is used to dry the air within the cavity of the hollow glass unit.
One-component, neutral, room temperature moisture curing silicone sealant. 1. Excellent flame-retardant performance, long time for fire blocking. 2. High elasticity and low modulus. It can be used with silicone fire-proof smoldering structural sealant that meets ETAG002 standard to provide 25-year quality guarantee. 3. Excellent resistance High and low temperature performance and weathering resistance performance 4. Neutral curing, no corrosion to the surface to be adhered 5. Good adhesion to most building materials and components without primer 6. It is stretching, connecting, and surrounding Ideal sealing material for sealing and fire blocking 7. Easy to use, it can be extruded at any time with a general glue gun. 8. Ring alignment
-
The well-packaged product can be stored for 12 months in a cool, ventilated, and dry place, and used before the "expiry date" of the outer packaging of the product
| TEST ITEMS |
TEST RESULTS |
TESTS1ANDARD |
| Base |
Polyisobutylene (PIB) |
- |
| Color |
Black |
- |
| Appearance |
Solid mass |
GB/T 1033.1 |
| Density |
1.1/1.25 fe/cm3] |
JC/T914 |
| Shear Strength |
0.21 MPa |
|
| Penetration (1 /1 Omm) |
25°C 40 |
|
| 130°C 290 |
JC/T 914 |
| Volatile Content |
Max. 0.02 % |
|
| Fogging |
Without visual fogging |
- |
| Moisture Vapour Transmission Rate (MVTR) |
0.26 [gr/m2.24hrs. 2mm] |
EN1279-4 |
| Gas Permeation Rate (Ar) |
1.30x10-3[gi7m2. hrs] |
EN1279-4 |
.APPLICATION FIELD
- One component, solvent free, non-fogging, permanently plastic butyl sealant, formulated for primary sealing of insulating glass units.
- It can keep its plastic and sealing properties in a wide temperature range.
- Excellent adhesion properties on glass, aluminum alloy, galvanized steel and stainless steel.
- Minimum moisture vapour and gas permeation.
- Excellent temperature stability: - 30°C to 80°C.
♦ TECHNICAL DATA - TYPICAL PROPERTIES
MF322 two-component polyurethane corner glue
Mainly used for bonding and sealing between aluminum alloy corners and profile cavities in aluminum alloy door and window structures; suitable for bonding wooden doors, windows and doors; for processed different materials, such as wood, building materials, ceramics and metals It has good adhesion.
How to use instructions
Remove dirt, dust, oil, frost, etc. on the surface of the substrate; place the plastic nozzle on the open bottle mouth and tighten it, and use a dedicated 1:1 double bottle glue gun to inject glue. Uncured glue can be cleaned with special cleaning agents (or other solvents such as alcohol).
Packaging
Packaging
1:1 double plastic bottle packaging: 600 ml per group; 9 groups per carton
Transport transmission
This product is non-hazardous and can be transported by train, car, ship and plane
Store
Can be stored for 6 months in a cool, ventilated and dry place.
Precautions and precautions
The initial 20g of mixed glue may be insufficiently mixed and is not recommended.
The glue mixed at room temperature should be used during the application period.
Avoid contact with skin and eyes. If inadvertently, rinse immediately with plenty of water and consult a doctor if necessary;
avoid contact with children; do not contaminate food, medicine or cosmetics.
The heavy workpiece to be bonded should be avoided to move before it is completely cured, and measures should be taken to fix it when it is necessary to move.
Recommended use conditions: temperature 15 ~ 35C, relative humidity 40% ~ 80%; if the temperature and humidity are lower than the recommended lower limit, the horn glue will cure more slowly, and if it is higher than the recommended upper limit, the construction time will be shortened.
Product Description
The MF910S is a warm side spacing that produces hollow glass. The MF910S is composed of a thermoplastic elastomer containing a desiccant, and the desiccant is used to dry the air within the cavity of the hollow glass unit.
Instructions for use
Cleaning, dry bonding surface, remove dust, oil and lipids. The MF910S is applied using a hollow glass production line to apply a special hot melt-dummy extruder, and the specific use conditions can be achieved by adjusting the temperature and pressure. The extrusion temperature ranges from 120 ° C to 140 ° C, and the ambient temperature requirement is not less than 18 ° C during construction.
Precautions
Before construction, please read the instructions, safety data sheets, packaging labels, and obtain information on safe use and harm your health.
Note: When using this hot melt glue or any other hot fused gum, appropriate care is carried out to avoid burns.
Range
The MF910S cannot be used as a structurate, which is mainly used for hollow glass production, and the two-component polysulfur seal adhesive assembly is used to complete the double seal. Dual sealing hollow glass produced by this product meets the requirements of GB / T11944.
Store
Best storage conditions: cool and ventilated, dry place storage period: 12 months (unopened packaging bucket)
Package
Iron drum packaging: 220kg (571.5mm) / barrel
Transportation
The MF910S is non-dangerous and can be transported through train, cars, ships and aircraft.
Important
The above mentioned parameters, especially those related to the application, is based on our trials and experience. Due to the use of materials and construction conditions, we recommend that you need to complete the necessary tests before use to ensure that our products can be better applied.