Mf910sg Thermoplastic Spacer for Glass Sealant

• Customization: Available
• Chemical Composition: Polyurethane Sealant
• Curing Time: Fast Curing: Within 24 Hours
• Model NO.: MF910SG
• Mildew Proof: Mildew Proof
• Usage: Industrial Manufacturing, Transportation
• Certificate: Ift Igma/Igcc TUV
• Delivery Time: 7 Days
• Material: Composite Materials
• State: Fluid
• Bonding Material: Glass
• After-Sales Service: 24 Hours After-Sales Service
• Type: Polysulfide Sealant
• Seal Tape Kind: Organic Materials
• Seal Tape Usage: Bonding
• Transport Package: Steel Drum
• Specification: 300KG+30KG
• Trademark: SILANDE
• Origin: China
• HS Code: 3214109000
• Production Capacity: 10000sets/Month
• Package Size: 21.00cm * 14.00cm * 18.00cm
• Package Gross Weight: 6.500kg
• Lead Time: 1 days (1 - 6000 ml) ; 3 days (6001 - 60000 ml) ; To be negotiated ( > 60000 ml)

Product Description

MF910SG Thermoplastic Spacer for IG

SILANDE MF910SG is the ultimate warm edge spacer for the manufacturing of insulating glass units, polyisobutylene(PIB) as the base, consisting of a thermoplastic elastomer formulated with the inclusion of desiccant for drying the airspace. Free of solvent, nonfogging and without sulfuration. It can keep its plasticity and sealing properties in wide temperature range and will not become harden and crack. It also has excellent resistance to air aging and perfect adhesion property to glass and rigidity. Meanwhile, it will compose an excellent anti-humidity system with elastic sealant due to its low moisture vapor transmission property.

APPLICATION FIELD
SILANDE MF910SG is used for the manufacturing of warm edge insulating glass units with varying shapes and air space widths. The recommended secondary sealant for use include SILANDE Two component, MF840 Polysulfide Sealant, MF881 Silicone Structural Sealant, and MF882 Silicone Sealant for IG.
♦ BASIC USE
The application surfaces must be clean, dry and free of dust and grease. Con tact with any solvent, oil, or plasticizer containing glazing materials should be avoided.

 . TECHNICAL DATA - TYPICAL PROPERTIES

Physical Properties
Test Items	Typical Values	Test Standard
Color	Black
Base	Synthetic Rubber(P),100% solid.
Specific Gravity	1.25 g/m^3	GB/T 1033.1
Shear Strength (0.5mm)	0.36 MPa	Q/ZZY 033
Penetration (1/10mm, 25°C)	25	GB/T 4509
Properties	Low moisture vapor transmission rate (MVTR), low gas permeability, low thermal conductivity.
Moisture Vapour Transmission Rate(MVTR)	0.17 [gr/m^2. 24hrs. 2mm]	EN1279-4
Gas Permeation Rate(Ar)	1.80 x 10-3 [gr/m^2. hrs]	EN1279-4
Tc Value	4.3%	EN1279-2
Service Temperature	-40°C to 80°C

SILANDE MF910SG can be applied by extruder special for thermoplastic spacer. Its concrete condition can be achieved by adjusting temperature and pressure. The preferred range of temperature is 100°C~140°C and operating environment temperature should be 18 °C or above. It is recommended that glazing material Compatibility & Adhesion Test is necessary before use.
 

♦ SHELF LIFE AND STORAGE
12 months stored in cool, dry and ventilated places below 30*C in the original unopened packing.

.PACKAGING
Steel drum: 220 kg/drum (<P 571.5mm)

TRANSPORTATION
Non-dangerous, can be transported by train, ship, automobile and plane.

.APPLICATION FIELD

• One component, solvent free, non-fogging, permanently plastic butyl sealant, formulated for primary sealing of insulating glass units.
• It can keep its plastic and sealing properties in a wide temperature range.
• Excellent adhesion properties on glass, aluminum alloy, galvanized steel and stainless steel.
• Minimum moisture vapour and gas permeation.
• Excellent temperature stability: - 30°C to 80°C.

♦ TECHNICAL DATA - TYPICAL PROPERTIES

TEST ITEMS	TEST RESULTS	TESTS1ANDARD
Base	Polyisobutylene (PIB)	-
Color	Black	-
Appearance	Solid mass	GB/T 1033.1
Density	1.1/1.25 fe/cm^3]	JC/T914
Shear Strength	0.21 MPa
Penetration (1 /1 Omm)	25°C 40
	130°C 290	JC/T 914
Volatile Content	Max. 0.02 %
Fogging	Without visual fogging	-
Moisture Vapour Transmission Rate (MVTR)	0.26 [gr/m^2.24hrs. 2mm]	EN1279-4
Gas Permeation Rate (Ar)	1.30x10-^3[gi7m^2. hrs]	EN1279-4

♦ APPLICATION INSTRUCTIONS

Hot Applied Butyl Sealant for Insulating Glass
Primary Sealant for the Manufacturing of Insulating Glass
.APPLICATION FIELD

• One component, solvent free, non-fogging, permanently plastic butyl sealant, formulated for primary sealing of insulating glass units.
• It can keep its plastic and sealing properties in a wide temperature range.
• Excellent adhesion properties on glass, aluminum alloy, galvanized steel and stainless steel.
• Minimum moisture vapour and gas permeation.
• Excellent temperature stability: - 30°C to 80°C.

♦ TECHNICAL DATA - TYPICAL PROPERTIES

TEST ITEMS	TEST RESULTS	TESTS1ANDARD
Base	Polyisobutylene (PIB)	-
Color	Black	-
Appearance	Solid mass	GB/T 1033.1
Density	1.1/1.25 fe/cm^3]	JC/T914
Shear Strength	0.21 MPa
Penetration (1 /1 Omm)	25°C 40
	130°C 290	JC/T 914
Volatile Content	Max. 0.02 %
Fogging	Without visual fogging	-
Moisture Vapour Transmission Rate (MVTR)	0.26 [gr/m^2.24hrs. 2mm]	EN1279-4
Gas Permeation Rate (Ar)	1.30x10-^3[gi7m^2. hrs]	EN1279-4

MF322 two-component polyurethane corner glue
Mainly used for bonding and sealing between aluminum alloy corners and profile cavities in aluminum alloy door and window structures; suitable for bonding wooden doors, windows and doors; for processed different materials, such as wood, building materials, ceramics and metals It has good adhesion.
How to use instructions
Remove dirt, dust, oil, frost, etc. on the surface of the substrate; place the plastic nozzle on the open bottle mouth and tighten it, and use a dedicated 1:1 double bottle glue gun to inject glue. Uncured glue can be cleaned with special cleaning agents (or other solvents such as alcohol).

Package and Delivery

Packaging
1:1 double plastic bottle packaging: 600 ml per group; 9 groups per carton

Transport transmission
This product is non-hazardous and can be transported by train, car, ship and plane

Store
Can be stored for 6 months in a cool, ventilated and dry place.

Precautions and precautions
The initial 20g of mixed glue may be insufficiently mixed and is not recommended.
The glue mixed at room temperature should be used during the application period.
Avoid contact with skin and eyes. If inadvertently, rinse immediately with plenty of water and consult a doctor if necessary;
avoid contact with children; do not contaminate food, medicine or cosmetics.
The heavy workpiece to be bonded should be avoided to move before it is completely cured, and measures should be taken to fix it when it is necessary to move.
Recommended use conditions: temperature 15 ~ 35C, relative humidity 40% ~ 80%; if the temperature and humidity are lower than the recommended lower limit, the horn glue will cure more slowly, and if it is higher than the recommended upper limit, the construction time will be shortened.