Mf613 Polyurethane Sealant for for Bonding of Substrates Such as Car Glass, Aluminum, Stainless Steel, and PVC

• Customization: Available
• Capacity: 600ml
• Color: White
• Model NO.: MF613
• Drying Time: 24 Hours
• Material: Composite Materials
• Usage: Construction, Industrial
• Type: Sealant
• State: Fluid
• Mildew Proof: Mildew Proof
• Seal Tape Kind: Organic Material
• Seal Tape Usage: Bonding
• Bonding Material: Glass, Aluminum, Stainless Steel, PVC
• Transport Package: Drum or Sausage
• Specification: 190L/drum 300ml or 600ml/pcs
• Trademark: SILANDE
• Origin: China
• HS Code: 3506919010
• Production Capacity: 8000000PCS/Year
• Package Size: 21.00cm * 14.00cm * 18.00cm
• Package Gross Weight: 6.500kg
• Lead Time: 1 days (1 - 6000 ML) ; 2 days (6001 - 60000 ML) ; To be negotiated ( > 60000 ML)

Product Description

MF613 polyurethane adhesive
MF613 polyurethane adhesive is a one-component polyurethane adhesive with high performance, elasticity and caulking after curing. It is cured by the moisture in the atmosphere to form a permanent elastic substance. MF613 is manufactured in strict accordance with the ISO9001/14001 quality assurance system and related protection regulations.

Features
Single component
Resistant
Low volatile odor
No solvent and PVC
Excellent construction characteristics
Flame retardant
Quick curing

Curing method
MF613 solidifies by reacting with moisture in the atmosphere. Generally, the lower the temperature, the lower the moisture content in the atmosphere, so the reaction process will also slow down.

Chemical resistance
MF613 is resistant to fresh water, acid, neutral and chlor-alkali-free cleaners; short-term resistant to fuel, mineral oil, animal fat and crude oil; not resistant to organic acids, concentrated mineral acids, lyes, bleaches and solvents. The above description is only a general guide. For special applications, we will provide suggestions on request.

Packaging Information
Hard packaging: 300 mI/piece
Flexible packaging: 600ml/piece
Vat: 190L/barrel.

Health and safety information
For information about transportation, handling, storage and chemical handling
The user should refer to the actual safety data sheet.

important
The above-mentioned relevant parameters of this product, especially relevant hints about application, are put forward on the basis of our test and experience. Due to the different materials and construction conditions, we recommend that you complete the necessary tests before use to ensure that our products can be better used.

Scope of application
MF613 is designed for the bonding of window glass in the OEM and repair markets. It is suitable for bonding glass, aluminum, stainless steel, PVC and other substrates. MF613 contains special stable ingredients to enhance its ability to resist ultraviolet rays, so it is especially suitable for sealing joints exposed to the outside. This product is only for users with professional skills. In order to ensure the bonding effect and the compatibility of the product with the material, tests should be done in advance under the actual substrate and environment.

Data foundation
All the data stated in the product data sheet are obtained from laboratory tests. As the environment is beyond our control, the actual measured data may be different.

♦ TECHNICAL DATA - TYPICAL PROPERTIES

TEST ITEMS	TEST RESULTS
COLOR	Component A (base) White Component B (catalyst) Black Mixture (A+B): Black
MIXING RATIO POT LIFE (23°C)	10:1(by weight) 20 min. Pot life is influenced by room conditions.
HARDING TIME	2-3 hrs, depending from pot life.
DENSITY	Com A[23°C] approx. 1.80 [g/cm^3] Com B [23°C] approx. 1.55 [g/cm^3]
VISCOSITY	Com A [23°C] 490 Pa.s ComB[23°C] 120 Pa.s
FINAL HARDNESS(ShoreA)	45 [Shore A]

MOISTURE VAPOUR TRANSMISSION (MVTR) 11 gr/m2.24hrs.2mm EN 1279/4
 

GAS PERMEATION(Ar)

6.63 x 10^-3 [gr/m^2.hrs] EN 1279/4

TENSILE ADHESION STRENGTH approx. 0.70 [MPa]
 

VOLATILE CONTENT(A+B)	<1.0%
FOGGING	Without visual fogging

Test Condition: As cured after 14 days at Temperature 23°C and 50% R.H.
 

• The well-packaged product can be stored for 12 months in a cool, ventilated, and dry place, and used before the "expiry date" of the outer packaging of the product
   

  TEST ITEMS	TEST RESULTS	TESTS1ANDARD
  Base	Polyisobutylene (PIB)	-
  Color	Black	-
  Appearance	Solid mass	GB/T 1033.1
  Density	1.1/1.25 fe/cm^3]	JC/T914
  Shear Strength	0.21 MPa
  Penetration (1 /1 Omm)	25°C 40
  	130°C 290	JC/T 914
  Volatile Content	Max. 0.02 %
  Fogging	Without visual fogging	-
  Moisture Vapour Transmission Rate (MVTR)	0.26 [gr/m^2.24hrs. 2mm]	EN1279-4
  Gas Permeation Rate (Ar)	1.30x10-^3[gi7m^2. hrs]	EN1279-4

  .APPLICATION FIELD

  • One component, solvent free, non-fogging, permanently plastic butyl sealant, formulated for primary sealing of insulating glass units.
  • It can keep its plastic and sealing properties in a wide temperature range.
  • Excellent adhesion properties on glass, aluminum alloy, galvanized steel and stainless steel.
  • Minimum moisture vapour and gas permeation.
  • Excellent temperature stability: - 30°C to 80°C.

  ♦ TECHNICAL DATA - TYPICAL PROPERTIES
  MF322 two-component polyurethane corner glue
  Mainly used for bonding and sealing between aluminum alloy corners and profile cavities in aluminum alloy door and window structures; suitable for bonding wooden doors, windows and doors; for processed different materials, such as wood, building materials, ceramics and metals It has good adhesion.
  How to use instructions
  Remove dirt, dust, oil, frost, etc. on the surface of the substrate; place the plastic nozzle on the open bottle mouth and tighten it, and use a dedicated 1:1 double bottle glue gun to inject glue. Uncured glue can be cleaned with special cleaning agents (or other solvents such as alcohol).
  
  Packaging

  

  

  Packaging
  1:1 double plastic bottle packaging: 600 ml per group; 9 groups per carton
  
  Transport transmission
  This product is non-hazardous and can be transported by train, car, ship and plane
  
  Store
  Can be stored for 6 months in a cool, ventilated and dry place.
  
  Precautions and precautions
  The initial 20g of mixed glue may be insufficiently mixed and is not recommended.
  The glue mixed at room temperature should be used during the application period.
  Avoid contact with skin and eyes. If inadvertently, rinse immediately with plenty of water and consult a doctor if necessary;
  avoid contact with children; do not contaminate food, medicine or cosmetics.
  The heavy workpiece to be bonded should be avoided to move before it is completely cured, and measures should be taken to fix it when it is necessary to move.
  Recommended use conditions: temperature 15 ~ 35C, relative humidity 40% ~ 80%; if the temperature and humidity are lower than the recommended lower limit, the horn glue will cure more slowly, and if it is higher than the recommended upper limit, the construction time will be shortened.