Still deciding? Get samples of $ !
Order Sample
|
| Customization: | Available |
|---|---|
| Adhesion Strength: | High Strength |
| Bonding Material: | Glass |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| TEST ITEMS | MEASURED VALUE | |
| Base | Appearance | White / Grey Ropy Paste |
| (Com A) | Viscosity | 170,000 mPa.S |
| Catalyst | Appearance | Black / White Ropy Paste |
| (Com B) | Viscosity | 80,000 mPa.S |
| As mixed | ||
| Appearance | Black / White / Grey | |
| Mixture | Viscosity | 340,000 mPa.S |
| By weight | Application Time (23°C, 50%) | 30-50 mins |
| (A:B = 14:1) | Tack-free Time (23°C, 50%) | 30-60 mins |
| Placed Vertical (50°C) | 0 | |
| Sag | Placed Horizontal | No deformation |
| Hardness | Shore A - 24h | 35 |
| Shore A-14 days | 44 | |
| As cured - after 14 days at T 23®C and 50% R.H. | ||
| 23°C | 0.97 MPa | |
| 90°C | 0.85 MPa | |
| Tensile | -30°C | 1.84 MPa |
| Adhesion | After Water Immersion | 1.01 MPa |
| Strength | After Water-UV Immersion | 0.97 MPa |
| Adhesive Failure Area | 0% | |
| 23°C Elongation Under Max. Tensile Strength | 140% | |
| Temperature Resistance | - 60~180°C | |
| Resistance to UV-Ozone | Continuous irradiation under water-UV 2500 hrs, No change. | |
| Moisture Vapour Transmission Rate (MVTR) | 17.7 [gr/m2.24hrs.2mm] - EN1279/4 | |
| Gas Permeation Rate (Ar) | 755 x 10-3 [gr/m2.hrs] - EN 1279/4 | |