Mf882 Two Component Silicone Sealant for Insulating Glass

• Type: Silicone Sealant
• Seal Tape Kind: Organic Silicone
• Seal Tape Usage: Insulating Glass Sealing
• Material: Composite Materials
• State: Fluid
• Mildew Proof: Mildew Proof
• Model NO.: MF882
• Bonding Material: Glass
• Transport Package: Barrel
• Specification: 190L+19L
• Trademark: SILANDE
• Origin: China
• HS Code: 3506919090
• Production Capacity: 50000 Sets/Month

Product Description

MF882 Two Component Silicone Sealant for Insulating Glass


Two Component Silicone Sealant for Insulating Glass

SILANDE MF882 is a two­ component neutral cured silicone sealant specifically developed for the manufacturing of insulating glass units used for window and door, vehicles and refrigeration, also can e used for edge frame curtain wall system. 


Excellent adhesion to a wide range of substrates including coated, enamelled and reflective glasses, anodised and polyester paint coated aluminium and stainless steel. 
Excellent temperature stability: - 60°C t 1ao0c. 
High level of mechanical properties. 
High elasticity and high modulus. 
Resistant to ozone. 

APPLICABLE STANDARDS 

EU Specification: EN1279 - part1, 2, 4, 6
China Specification: GB29755, JC/T471. 
IGCC-IGMA Approved.  

SHELF LIFE AND STORAGE

12 months from the date of production below 30°C. 

PACKAGING

A: 265KG B: 19KG 
 

TYPICAL PROPERTIES
	TEST ITEMS	MEASURED VALUE
Base	Appearance	White / Grey Ropy Paste
(Com A)	Viscosity	150,000 mPa.S
Catalyst	Appearance	Black / White Ropy Paste
(Com B)	Viscosity	80,000 mPa.S
Mixture	Appearance	Black / White / Grey
By weight	Application Time (23°C, 50%)	30-50 mins
(A:B = 16:1)	Tack-free Time (23°C, 50%)	30-60 mins
	Placed Vertically (50°C)	0
	Placed Horizontal	No deformation
	Shore A - 4h	22
Hardness	Shore A - 24h	40
	Shore A-14 days	46
After 14 days at a temperature of 23°C and RH 50%.
Elastic Recovery		94%
Adhesion Property at Definite Elongation		No Damage
	23°C	0.92 MPa
	After Aging in Hot Air	1.10 MPa
Tensile	300 hr After Water-UV	0.82 MPa
Adhesion	-20°C	1.28 MPa
Strength	60°C	0.85 MPa
	After Water-UV Immersion	0.79 MPa
	Adhesive Failure Area	0%
Elongation under maximum tensile strength at 23°C 93%
	TGA	3.6%
Moisture Vapour Transmission Rate (MVTR)		12.3 [gr/m^2.24hrs.2mm] - EN1279/4
Gas Permeation Rate (Ar)		360 x 10-3 rgr/m^2.hrsl - EN1279/4