Advanced Non-Drying Anti-Corrosion Sealant for Bridges and Ships

• Customization: Available
• Adhesion Strength: High Strength
• Bonding Material: Aluminum
• Model NO.: MF2000G
• Color: Black
• Usage: Construction, Transportation
• Transport Package: Barrel
• Specification: 25 Kg / barrel 245 Kg / barrel
• Trademark: SILANDE
• Origin: China
• HS Code: 3506919010
• Production Capacity: 8000000barrels/Year
• Package Size: 21.00cm * 14.00cm * 18.00cm
• Package Gross Weight: 6.500kg
• Lead Time: 1 days (1 - 6000 ml) ; 2 days (6001 - 60000 ml) ; To be negotiated ( > 60000 ml)

Product Description

MF2000G Non-vulcanized Non-drying Anti-corrosion Sealant

.APPLICATION FIELD

• One component, solvent free, non-fogging, permanently plastic butyl sealant, formulated for primary sealing of insulating glass units.
• It can keep its plastic and sealing properties in a wide temperature range.
• Excellent adhesion properties on glass, aluminum alloy, galvanized steel and stainless steel.
• Minimum moisture vapour and gas permeation.
• Excellent temperature stability: - 30°C to 80°C.

♦ TECHNICAL DATA - TYPICAL PROPERTIES

TEST ITEMS	TEST RESULTS	TESTS1ANDARD
Base	Polyisobutylene (PIB)	-
Color	Black	-
Appearance	Solid mass	GB/T 1033.1
Density	1.1/1.25 fe/cm^3]	JC/T914
Shear Strength	0.21 MPa
Penetration (1 /1 Omm)	25°C 40
	130°C 290	JC/T 914
Volatile Content	Max. 0.02 %
Fogging	Without visual fogging	-
Moisture Vapour Transmission Rate (MVTR)	0.26 [gr/m^2.24hrs. 2mm]	EN1279-4
Gas Permeation Rate (Ar)	1.30x10-^3[gi7m^2. hrs]	EN1279-4

♦ APPLICATION INSTRUCTIONS

Hot Applied Butyl Sealant for Insulating Glass
Primary Sealant for the Manufacturing of Insulating Glass
.APPLICATION FIELD

• One component, solvent free, non-fogging, permanently plastic butyl sealant, formulated for primary sealing of insulating glass units.
• It can keep its plastic and sealing properties in a wide temperature range.
• Excellent adhesion properties on glass, aluminum alloy, galvanized steel and stainless steel.
• Minimum moisture vapour and gas permeation.
• Excellent temperature stability: - 30°C to 80°C.

♦ TECHNICAL DATA - TYPICAL PROPERTIES

TEST ITEMS	TEST RESULTS	TESTS1ANDARD
Base	Polyisobutylene (PIB)	-
Color	Black	-
Appearance	Solid mass	GB/T 1033.1
Density	1.1/1.25 fe/cm^3]	JC/T914
Shear Strength	0.21 MPa
Penetration (1 /1 Omm)	25°C 40
	130°C 290	JC/T 914
Volatile Content	Max. 0.02 %
Fogging	Without visual fogging	-
Moisture Vapour Transmission Rate (MVTR)	0.26 [gr/m^2.24hrs. 2mm]	EN1279-4
Gas Permeation Rate (Ar)	1.30x10-^3[gi7m^2. hrs]	EN1279-4

MF322 two-component polyurethane corner glue
Mainly used for bonding and sealing between aluminum alloy corners and profile cavities in aluminum alloy door and window structures; suitable for bonding wooden doors, windows and doors; for processed different materials, such as wood, building materials, ceramics and metals It has good adhesion.
How to use instructions
Remove dirt, dust, oil, frost, etc. on the surface of the substrate; place the plastic nozzle on the open bottle mouth and tighten it, and use a dedicated 1:1 double bottle glue gun to inject glue. Uncured glue can be cleaned with special cleaning agents (or other solvents such as alcohol).

Package and Delivery

Packaging
1:1 double plastic bottle packaging: 600 ml per group; 9 groups per carton

Transport transmission
This product is non-hazardous and can be transported by train, car, ship and plane

Store
Can be stored for 6 months in a cool, ventilated and dry place.

Precautions and precautions
The initial 20g of mixed glue may be insufficiently mixed and is not recommended.
The glue mixed at room temperature should be used during the application period.
Avoid contact with skin and eyes. If inadvertently, rinse immediately with plenty of water and consult a doctor if necessary;
avoid contact with children; do not contaminate food, medicine or cosmetics.
The heavy workpiece to be bonded should be avoided to move before it is completely cured, and measures should be taken to fix it when it is necessary to move.
Recommended use conditions: temperature 15 ~ 35C, relative humidity 40% ~ 80%; if the temperature and humidity are lower than the recommended lower limit, the horn glue will cure more slowly, and if it is higher than the recommended upper limit, the construction time will be shortened.

MF2000G is a one-component non-vulcanized, neutral non-drying anticorrosive sealant. It has unique water absorption and corrosion resistance. It also has good sealing, water resistance and aging resistance. It is resistant to metal, glass, and ceramics. And other materials have good adhesion type. MF2000G is suitable for filling and sealing of cable ducts of suspension bridges and cable-stayed bridges, as well as caulking and sealing of expansion joints and peripheral joints of ships and buildings.

Introduction:
MF2000G is a single component non-vulcanized, neutral cured, non-drying, rubber sealant. It has good flexibility and scalability, and also good sealing, water resistance and resistance to aging. Good adhesion with metal, glass , ceramics and other materials. No agglomeration and crack over a wide temperature range.
Purposes:
Mainly applied for caulking sealing to shipbuilding, construction joints, peripheral joints and the gapfilling seal to suspension bridge and cable conduit of cable-stayed bridge.
Instruction manual:
Washing and drying the adhesive surface to remove dirt, oil, fat and rust and other debris. Please refer to"Manual of Construction".
Storage:
24 months stored in cool, ventilated and dry place.
Package:
25Kg / barrel, 245 Kg / barrel
Note: You can also be customized according to user needs.
Transportation:
MF2000G is non-dangerous goods, can be transported by train, car, ship and airplane.
IMPORTANT
Above-mentioned are the relevant parameters on the product, particularly with regard to the application for tips, it is based on our tests and experience. Due to the use of different materials and construction conditions, we recommend that you use to complete before the necessary tests to ensure that our products can be better used.