CHICO Brand Adsorbent for insulating glass fully cover the current requirement of EN1279-4 and 6, it not only technical can meet the requirement of EN1279 but also it can save money for the end-users in the parameters of lower density , higher adsorption capacity and also it will safeguard your IG unit in the ideal way together with other insulating glass components-Primary sealant, Secondary sealant, and Spacer bar.
Please refer to the parameters in the following:
| Item |
unit |
|
Bead |
|
| Diameter |
mm |
0.5-0.9 |
1.0-1.5 |
1.5-2.0 |
| Delta T |
ºC |
≥35 |
≥35 |
≥35 |
Static H2O adsorption
(10%RH,@25C) |
% wt |
≥16 |
≥16 |
≥16 |
| Bulk Density |
g/ml |
≥0.75 |
≥0.75 |
≥0.75 |
| Particle ratio |
% |
≥98 |
≥98 |
≥98 |
| Gas Desorption |
Ml/g |
≤0.28 |
≤0.28 |
≤0.28 |
| Loss on Ignition(540C) |
% wt |
≤1.5 |
≤1.5 |
≤1.5 |
- Properties
- No corrosiveness
- High compressive strength
- High adsorption capacity
- High Delta T value
- Good capacity in controlling
adsorption-speed
- Low moisture residence
- Low nitrogen adsorption
- Low electrostatic load
- Low dust level
- Uniform granulation
1. Molecular Sieve
Molecular sieve (also known as synthetic zeolite) is a kind of aluminosilicate microporous mesh crystal, composed of SiO2 and Al2O3 tetrahedra, with uniform pore size (about a few angstroms) and extremely large surface area. There are metal cations (such as Na+, K+, Ca2+, etc.) in the molecular sieve lattice to balance the excess negative charges in the tetrahedron. Different types of molecular sieves have different pore sizes or shapes, and can be used to separate a variety of different molecules. Water is a very polar molecule. Type A molecular sieve has a very high affinity with water, and is often used as a desiccant with excellent effects. The molecular sieve we are talking about here refers to a 3A (1A=10-10m) molecular sieve that can only be used to absorb water molecules. It is dozens of times higher in drying capacity and depth than silica gel desiccant, alumina desiccant and any other types of clay desiccants.
3A molecular sieve and insulating glass desiccant
In view of the description in 2, when the temperature is slightly reduced, other types of molecular sieves will adsorb a large amount of air in the hollow glass, resulting in a vacuum state; when the temperature rises, the molecular sieve will release a large amount of air into the spacer layer, resulting in hollow The air in the glass expands. With the change of temperature difference between day and night and the changing of seasons, insulating glass is easily distorted and broken due to expansion and contraction, shortening its life span, and sudden breaking of glass will cause major safety accidents. Therefore, it is strictly forbidden to use non-3A molecular sieve as the hollow glass with dry air. Desiccant.
4. Green Energy 3A Molecular Sieve (Insulating Glass Desiccant)
As a special desiccant for insulating glass, 3A molecular sieve can best meet all the performance indexes of insulating glass without any influence on its physical and chemical properties. It can continuously and deeply adsorb the water and residual organic matter in the insulating glass spacer layer, effectively prevent the condensation and frost of the glass, completely solve the problem of distortion and breakage caused by the expansion or contraction of the insulating glass, and ensure that the insulating glass is as short as 20 years -8ºC Dew point life. Therefore, only 3A molecular sieve can be used as an insulating glass desiccant.