TEST ITEMS | TECHNICAL DATA | TEST RESULT | STANDARD |
Uncured-Test Conditions: T: (23±2)°C, (50±5)% R.H. | |||
Rheological (Flow) Properties | Vertical displacement: sagW4.8 Horizontal displacement: No deformation |
Vertical displacement: 0 mm sag Horizontal displacement: no deformation |
ASTM C639 |
Extrudability, ml/min | ,10 | 52.2 | ASTM C1183 |
Tack-free Time, h Curing Time, d |
W3 / |
2.5 7~14 |
ASTM C679 |
Range of Application Temperature, °C | / | 5~40 | / |
After cured-Test Conditions: 28 days placed at T: (23±2)°C, (50±5)% R.H. | |||
Hardness, Shore A | 15-50 | 40 | ASTM C661 |
Movement capability % | ±50 | ±50 | ASTM C719 |
Range ofTemperature Resistance, °C |
/ | -60~180°C | 1 |
Effects of Heat Aging | Shall lose W7% of its original weight Weight loss: 2.2% or show no cracking and chalking No cracking | ASTM C1246 | |
Staining and Color Change | The sealant shall not cause any visible stain on the top surface of a white cement mortar bases | There was no visible stain on the top surface of a white cement mortar bases | ASTM C510 |
Adhesion&Cohesion under Cyclic Movement | W9 cm2 | No loss in bond | ASTM C719 |
Adhesion-in-Peel | The peel strength shall N22.2 (5lbf) and the sealant shall showW25% bond loss | 104.1N (Substrate:Glass) 70.5 (Substrate: Aluminium)Cohesive failure, no adhesion bond loss between sealant and surface | ASTM C794 |