Mf840 Two Components Polysulfide Sealant Fbr Insulating Glass Secondary Sealant for The Manufacturing of Insulating Glass

• Customization: Available
• Adhesion Strength: High Strength
• Bonding Material: Glass
• Model NO.: MF840
• Color: Black
• Usage: Construction
• Transport Package: Drum
• Specification: MF840 big barrel: A 300 Kg/barrel +B 30 Kg/barrel
• Trademark: SILANDE
• Origin: China
• HS Code: 3506919010
• Production Capacity: 50000PCS/Years
• Package Size: 120.00cm * 85.00cm * 85.00cm
• Package Gross Weight: 330.000kg
• Lead Time: 1 days (1 - 330 kg) ; 2 days (331 - 3300 kg) ; To be negotiated ( > 3300 kg)

Product Description

Mf840 Two Component Polysulfide Sealant for Insulating Glass
♦ MIXING AND DISPENSING INSTRUCTIONS
Ensure that SILANDE MF840 is mixed thoroughly and remains air-bubble free, adhering to the precise ratio.
For optimal performance, mix SILANDE MF840 in a base to curing agent ratio of 10:1 by weight, or 8.6:1 by volume. This mix ratio typically provides a working time of 20-30 minutes and allows units to be handled within 6-8 hours. Slight deviations are permissible, but should stay within 100:6 to 100:12 by weight to maintain minimum properties.
Mixing Ratio by Weight 100:6 100:8100:10 100:12
Mixing Ratio by Volume 14.3:1 10.7:18.6:1 7.1:1

 

. CURING
When SILANDE MF840A base is mixed with+SILANDE MF840 B catalyst at a 10:1 weight ratio, it becomes tack-free in about 25-35 minutes at ambient conditions of 23°C,50%R.H. The IGUs can be transported to the project after 3 days. Full properties develop within 5 days as curing by-products evaporate, although it may take longer in colder climates.
Ensure successful adhesion and compatibility tests are conducted before commencing the project.
TECHNICAL DATA-TYPICAL PROPERTIES

TEST ITEMS	TEST RESULTS
COLOR	Component A (base) White Component B (catalyst) Black Mixture (A+B): Black
MIXING RATIO POT LIFE (23°C)	10:1(by weight) 20 min. Pot life is influenced by room conditions.
HARDING TIME	2-3 hrs, depending from pot life.
DENSITY	Com A[23°C] approx. 1.80 [g/cm^3] Com B [23°C] approx. 1.55 [g/cm^3]
VISCOSITY	Com A [23°C] 490 Pa.s ComB[23°C] 120 Pa.s
FINAL HARDNESS(ShoreA)	45 [Shore A]

 

MOISTURE VAPOUR TRANSMISSION (MVTR)
11 gr/m2.24hrs.2mm
EN 1279/4

GAS PERMEATION(Ar)

6.63 x 10^-3 [gr/m^2.hrs] EN 1279/4

 

TENSILE ADHESION STRENGTH
approx. 0.70 MPa
 

VOLATILE CONTENT(A+B)	<1.0%
FOGGING	Without visual fogging

 

Test Condition: Cured after 14 days at 23°C and
50%
R.H.
. SHELF LIFE AND STORAGE
Store below 30°C for up to 12 months from the production date.
The MF-840 series is a solvent-free, two-component, room-temperature curing elastic sealant with excellent bonding properties, suitable for materials such as glass, aluminum alloy, and galvanized steel.

The MF840 series consists of two components: A (base paste) which is a white, uniform, delicate paste, and B (curing paste) which is black, uniform, and delicate. The recommended mix ratio is A:B = 100: (6-12) by weight, with 100:10 being ideal.
The primary application of the MF840 series sealant is in the production of insulating glass.
Insulating glass: This innovative product consists of two or more glass panes, meticulously supported, evenly spaced, and securely bonded and sealed around the perimeter. This construction creates a dry gas space between the glass layers, ensuring optimal insulation and energy efficiency.

MF840 series sealant: Designed for versatility, our MF840 series sealant can be paired with butyl sealant, with butyl serving as the primary seal and polysulfide as the secondary (outer) seal. Additionally, it is adept at sealing single-channel insulating glass, offering robust and reliable protection.