High-Performance Mf910h Butyl Hotmelt Sealant for Insulating Glass

• Customization: Available
• Capacity: 600ml
• Color: Black
• Model NO.: MF910H
• Drying Time: 24 Hours
• Material: Polysulfide
• Usage: Automotive, Construction, Industrial
• Delivery: 7-10days
• Certification: Igma/Igcc Approved
• Transport Package: Box
• Specification: 6.5 kg/box 220 kg/drum (0571.5mm)
• Trademark: SILANDE
• Origin: China
• HS Code: 3506919010
• Production Capacity: 5000000PCS/Years
• Package Size: 21.00cm * 14.00cm * 18.00cm
• Package Gross Weight: 6.500kg
• Lead Time: 1 days (1 - 6000 ml) ; 3 days (6001 - 60000 ml) ; To be negotiated ( > 60000 ml)

Product Description

MF910H Hotmelt Sealant for Insulating Glass
Secondary Sealant for the Manufacturing of Insulating Glass

.APPLICATION FIELD

• One component, solvent free, non-fogging, permanently plastic butyl sealant, formulated for primary sealing of insulating glass units.
• It can keep its plastic and sealing properties in a wide temperature range.
• Excellent adhesion properties on glass, aluminum alloy, galvanized steel and stainless steel.
• Minimum moisture vapour and gas permeation.
• Excellent temperature stability: - 30°C to 80°C.

♦ TECHNICAL DATA - TYPICAL PROPERTIES

TEST ITEMS	TEST RESULTS	TESTS1ANDARD
Base	Polyisobutylene (PIB)	-
Color	Black	-
Appearance	Solid mass	GB/T 1033.1
Density	1.1/1.25 fe/cm^3]	JC/T914
Shear Strength	0.21 MPa
Penetration (1 /1 Omm)	25°C 40
	130°C 290	JC/T 914
Volatile Content	Max. 0.02 %
Fogging	Without visual fogging	-
Moisture Vapour Transmission Rate (MVTR)	0.26 [gr/m^2.24hrs. 2mm]	EN1279-4
Gas Permeation Rate (Ar)	1.30x10-^3[gi7m^2. hrs]	EN1279-4

♦ APPLICATION INSTRUCTIONS

Hot Applied Butyl Sealant for Insulating Glass
Primary Sealant for the Manufacturing of Insulating Glass
.APPLICATION FIELD

• One component, solvent free, non-fogging, permanently plastic butyl sealant, formulated for primary sealing of insulating glass units.
• It can keep its plastic and sealing properties in a wide temperature range.
• Excellent adhesion properties on glass, aluminum alloy, galvanized steel and stainless steel.
• Minimum moisture vapour and gas permeation.
• Excellent temperature stability: - 30°C to 80°C.

♦ TECHNICAL DATA - TYPICAL PROPERTIES

TEST ITEMS	TEST RESULTS	TESTS1ANDARD
Base	Polyisobutylene (PIB)	-
Color	Black	-
Appearance	Solid mass	GB/T 1033.1
Density	1.1/1.25 fe/cm^3]	JC/T914
Shear Strength	0.21 MPa
Penetration (1 /1 Omm)	25°C 40
	130°C 290	JC/T 914
Volatile Content	Max. 0.02 %
Fogging	Without visual fogging	-
Moisture Vapour Transmission Rate (MVTR)	0.26 [gr/m^2.24hrs. 2mm]	EN1279-4
Gas Permeation Rate (Ar)	1.30x10-^3[gi7m^2. hrs]	EN1279-4

MF322 two-component polyurethane corner glue
Mainly used for bonding and sealing between aluminum alloy corners and profile cavities in aluminum alloy door and window structures; suitable for bonding wooden doors, windows and doors; for processed different materials, such as wood, building materials, ceramics and metals It has good adhesion.
How to use instructions
Remove dirt, dust, oil, frost, etc. on the surface of the substrate; place the plastic nozzle on the open bottle mouth and tighten it, and use a dedicated 1:1 double bottle glue gun to inject glue. Uncured glue can be cleaned with special cleaning agents (or other solvents such as alcohol).

Package and Delivery

Packaging
1:1 double plastic bottle packaging: 600 ml per group; 9 groups per carton

Transport transmission
This product is non-hazardous and can be transported by train, car, ship and plane

Store
Can be stored for 6 months in a cool, ventilated and dry place.

Precautions and precautions
The initial 20g of mixed glue may be insufficiently mixed and is not recommended.
The glue mixed at room temperature should be used during the application period.
Avoid contact with skin and eyes. If inadvertently, rinse immediately with plenty of water and consult a doctor if necessary;
avoid contact with children; do not contaminate food, medicine or cosmetics.
The heavy workpiece to be bonded should be avoided to move before it is completely cured, and measures should be taken to fix it when it is necessary to move.
Recommended use conditions: temperature 15 ~ 35C, relative humidity 40% ~ 80%; if the temperature and humidity are lower than the recommended lower limit, the horn glue will cure more slowly, and if it is higher than the recommended upper limit, the construction time will be shortened.

♦ APPLICATION FIELD
One component, solvent free, non-fogging, permanently plastic butyl sealant, formulated for secondary sealing of insulating glass units.

• It can keep its plastic and sealing properties in a wide temperature range.
• Excellent adhesion properties on glass, aluminum alloy, galvanized steel and stainless steel.
• Immediate high strength development for superior handing and transportation capabilities.
• Excellent slump resistance, resulting in reduced after application tooling.
• Low after-application tack for easy of handing.
• Minimum moisture vapour and gas permeation.
• Excellent temperature stability: - 30°C to 80°C.
• DESCRIPTION
  SILANDE MF910H is a hot melt sealant formulated for single seal insulating glass. This product has been designed for insulating glass manufacturers running hand applied, semi automated, and linear extruded operations.
• 

  

  
•  TECHNICAL DATA - TYPICAL PROPERTIES

  TEST ITEMS	TEST RESULTS	TEST STANDARD
  Color	Black	-
  Consistency	100% Solid mass	-
  Density	Approx. 1.18 [g/cm^3]	GB/T 1033.1
  Shear Strength	0.25 MPa	Q/ZZY 031
  Penetration (1/10mm, 25°C)	28	GB/T 4509
  Volatile Content (130°C, 50 hrs)	Max. 0.02 %	-
  Elongation at Yield	Approx. 20%	Q/ZZY 031
  Moisture Vapour Transmission Rate (MVTR)	0.39 [gr/m^2. 24hrs. 2mm]	EN1279-4
  Gas Permeation Rate (Ar)	1.48x 10^-3 [gr/m^2. hrs]	EN1279-4

• APPLICABLE STANDARDS
• • EU Specification: EN1279 - part 4
• SHELF LIFE AND STORAGE
• 24 months stored in cool, dry and ventilated places.
  . PACKAGING
  6.5 kg/box 220 kg/drum (0571.5mm)