Mf882 Silicone Sealant for Sealing of Insulating Glass in Construction, Transportation, Refrigeration and Other Industries.

• Adhesion Strength: High Strength
• Bonding Material: Glass
• Color: Black
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: MF882
• Usage: Electronics, Construction, Transportation
• Certificate: Ift Igma/Igcc TUV
• Delivery Time: 7 Days
• Transport Package: Steel Drum
• Specification: 200L iron drum 20L plastic barrel
• Trademark: SILANDE
• Origin: China
• HS Code: 3214109000
• Production Capacity: 100000sets/Month
• Package Size: 120.00cm * 85.00cm * 85.00cm
• Package Gross Weight: 209.000kg
• Lead Time: 1 days (1 - 1 Sets) ; 2 days (2 - 10 Sets) ; To be negotiated ( > 10 Sets)

Product Description

MF882 is a two-component room temperature curing silicone insulating glass sealant. It has excellent weathering resistance and the curing time can be adjusted.
Neutral curing, no corrosion to the adhered surface
Fast curing, with high bond strength after curing
No pollution to the environment
Excellent high and low temperature resistance and weathering resistance
Good adhesion to most building materials such as glass and aluminum
 

TYPICAL PROPERTIES
	TEST ITEMS	MEASURED VALUE
Base	Appearance	White / Grey Ropy Paste
(Com A)	Viscosity	150,000 mPa.S
Catalyst	Appearance	Black / White Ropy Paste
(Com B)	Viscosity	80,000 mPa.S
Mixture	Appearance	Black / White / Grey
By weight	Application Time (23°C, 50%)	30-50 mins
(A:B = 16:1)	Tack-free Time (23°C, 50%)	30-60 mins
	Placed Vertically (50°C)	0
	Placed Horizontal	No deformation
	Shore A - 4h	22
Hardness	Shore A - 24h	40
	Shore A-14 days	46
After 14 days at a temperature of 23°C and RH 50%.
Elastic Recovery		94%
Adhesion Property at Definite Elongation		No Damage
	23°C	0.92 MPa
	After Aging in Hot Air	1.10 MPa
Tensile	300 hr After Water-UV	0.82 MPa
Adhesion	-20°C	1.28 MPa
Strength	60°C	0.85 MPa
	After Water-UV Immersion	0.79 MPa
	Adhesive Failure Area	0%
Elongation under maximum tensile strength at 23°C 93%
	TGA	3.6%
Moisture Vapour Transmission Rate (MVTR)		12.3 [gr/m^2.24hrs.2mm] - EN1279/4
Gas Permeation Rate (Ar)		360 x 10-3 rgr/m^2.hrsl - EN1279/4

Silicone salant series products: we have six professional research laboratories, which are engaged in the research and development of series products such as polysulfide, silicone, butyl, polyurethane, epoxy, organic silicon, adhesive film, as well as the research and development of supporting production and testing equipment. The company has introduced multiple fully automatic sealant production lines from abroad, and through digestion, absorption, and further improvement, the annual production capacity of sealant is nearly 10000 tons.

For the past thirty years, we have formed a multi-level scientific research team from academicians to bachelor's degree, with nearly a hundred scientific researchers participating in and formulating dozens of standards and industry standards. It is a high-tech enterprise with strong research and development capabilities in the domestic sealant industry. The company has strong technical strength, advanced and complete production and testing equipment. We have a world leading fully automatic production line for polysulfide, silicone, butyl, and polyurethane sealants; We are a domestic enterprise that has established testing methods for silicone structural sealants in accordance with the "EU Silicone Structural Sealant" standard. We have independently developed and introduced a complete set of testing equipment required by the "EU Silicone Structural Sealant" standard, and have applied for dozens of national projects.