Mf6009 High-Speed Rail Special Structural Adhesive Film

• Customization: Available
• Adhesion Strength: High Strength
• Bonding Material: Glass
• Model NO.: MF6009
• Color: White
• Usage: Construction
• Type: Sealing Strip
• Material: Composite Materials
• State: Nonfluid
• Mildew Proof: Mildew Proof
• Seal Tape Kind: Organic Material
• Seal Tape Usage: Bonding
• Transport Package: Carton
• Specification: 300mm-1000mm
• Trademark: SILANDE
• Origin: China
• HS Code: 3506919010
• Production Capacity: 500000rolls/Years
• Package Size: 21.00cm * 14.00cm * 18.00cm
• Package Gross Weight: 6.500kg
• Lead Time: 1 days (1 - 6000 ml) ; 3 days (6001 - 60000 ml) ; To be negotiated ( > 60000 ml)

Product Description

MF6009 high-speed rail special structural adhesive film
MF6009 high-speed rail special structural adhesive film is a composite structural adhesive film of epoxy resin and nitrile butadiene rubber. It has high strength, good toughness, fast curing at high temperature, and is compatible with board-board, board-core bonding composite structural film. , The thickness is uniform, the amount of glue is accurate, the construction process is simple, and the overall performance and bonding reliability are high. MF6009 is manufactured in strict accordance with the ISO9001/14001 quality assurance system and related protection regulations.

product description:
MF6009 high-speed rail structural adhesive film is a composite structural adhesive film of epoxy resin and nitrile rubber. It has high strength, good toughness, fast curing at high temperature, compatible with board-board, board-core bonding composite structural film , The thickness is uniform, the amount of glue is accurate, the construction process is simple, and the overall performance and bonding reliability are high. MF6009 is manufactured in strict accordance with the |SO9001 /14001 quality assurance system and related protection regulations.

Product superiority:
Composite film
Quick curing
1-2mm climb after curing
High strength
Excellent construction characteristics
Hot melt film forming without solvent

Scope of application:
MF6009 is mainly used for the bonding of high-speed rail doors, and is suitable for bonding of aluminum alloy, steel and other metal materials. MF6009 has pressure-sensitive adhesive on both sides, which can be directly pasted at room temperature, easy to operate, fast curing, high strength, good toughness, compatible with board-board, board-core bonding, and has a 1-2mm climb after high temperature curing Characteristics.
This product is only for users with professional skills. In order to ensure the bonding effect and the compatibility of the product with the material, tests should be done in advance under the actual substrate and environment.

Curing method
Mf6009 is a structural adhesive film cured at medium temperature, and the curing conditions are:
30~35 minutes at 140C, 0.3MPa;
60~75 minutes at 130°C and 0.3MPa.

Chemical resistance
MF6009 is resistant to dilute salt water, low-concentration acid and low-concentration lye; short-term resistance to fuel, mineral oil, animal fat and crude oil; not resistant to high-concentration acid and lye. The above description is only a general guide, for special applications we will provide suggestions on request.
♦ TECHNICAL DATA - TYPICAL PROPERTIES

TEST ITEMS	TEST RESULTS
COLOR	Component A (base) White Component B (catalyst) Black Mixture (A+B): Black
MIXING RATIO POT LIFE (23°C)	10:1(by weight) 20 min. Pot life is influenced by room conditions.
HARDING TIME	2-3 hrs, depending from pot life.
DENSITY	Com A[23°C] approx. 1.80 [g/cm^3] Com B [23°C] approx. 1.55 [g/cm^3]
VISCOSITY	Com A [23°C] 490 Pa.s ComB[23°C] 120 Pa.s
FINAL HARDNESS(ShoreA)	45 [Shore A]

MOISTURE VAPOUR TRANSMISSION (MVTR) 11 gr/m2.24hrs.2mm EN 1279/4
 

GAS PERMEATION(Ar)

6.63 x 10^-3 [gr/m^2.hrs] EN 1279/4

TENSILE ADHESION STRENGTH approx. 0.70 [MPa]
 

VOLATILE CONTENT(A+B)	<1.0%
FOGGING	Without visual fogging

Test Condition: As cured after 14 days at Temperature 23°C and 50% R.H.
 

• The well-packaged product can be stored for 12 months in a cool, ventilated, and dry place, and used before the "expiry date" of the outer packaging of the product
   

  TEST ITEMS	TEST RESULTS	TESTS1ANDARD
  Base	Polyisobutylene (PIB)	-
  Color	Black	-
  Appearance	Solid mass	GB/T 1033.1
  Density	1.1/1.25 fe/cm^3]	JC/T914
  Shear Strength	0.21 MPa
  Penetration (1 /1 Omm)	25°C 40
  	130°C 290	JC/T 914
  Volatile Content	Max. 0.02 %
  Fogging	Without visual fogging	-
  Moisture Vapour Transmission Rate (MVTR)	0.26 [gr/m^2.24hrs. 2mm]	EN1279-4
  Gas Permeation Rate (Ar)	1.30x10-^3[gi7m^2. hrs]	EN1279-4

  .APPLICATION FIELD

  • One component, solvent free, non-fogging, permanently plastic butyl sealant, formulated for primary sealing of insulating glass units.
  • It can keep its plastic and sealing properties in a wide temperature range.
  • Excellent adhesion properties on glass, aluminum alloy, galvanized steel and stainless steel.
  • Minimum moisture vapour and gas permeation.
  • Excellent temperature stability: - 30°C to 80°C.

  ♦ TECHNICAL DATA - TYPICAL PROPERTIES
  MF322 two-component polyurethane corner glue
  Mainly used for bonding and sealing between aluminum alloy corners and profile cavities in aluminum alloy door and window structures; suitable for bonding wooden doors, windows and doors; for processed different materials, such as wood, building materials, ceramics and metals It has good adhesion.
  How to use instructions
  Remove dirt, dust, oil, frost, etc. on the surface of the substrate; place the plastic nozzle on the open bottle mouth and tighten it, and use a dedicated 1:1 double bottle glue gun to inject glue. Uncured glue can be cleaned with special cleaning agents (or other solvents such as alcohol).
  
  Packaging

  

  

  Packaging
  1:1 double plastic bottle packaging: 600 ml per group; 9 groups per carton
  
  Transport transmission
  This product is non-hazardous and can be transported by train, car, ship and plane
  
  Store
  Can be stored for 6 months in a cool, ventilated and dry place.
  
  Precautions and precautions
  The initial 20g of mixed glue may be insufficiently mixed and is not recommended.
  The glue mixed at room temperature should be used during the application period.
  Avoid contact with skin and eyes. If inadvertently, rinse immediately with plenty of water and consult a doctor if necessary;
  avoid contact with children; do not contaminate food, medicine or cosmetics.
  The heavy workpiece to be bonded should be avoided to move before it is completely cured, and measures should be taken to fix it when it is necessary to move.
  Recommended use conditions: temperature 15 ~ 35C, relative humidity 40% ~ 80%; if the temperature and humidity are lower than the recommended lower limit, the horn glue will cure more slowly, and if it is higher than the recommended upper limit, the construction time will be shortened.