Material: | Silicone, Composite Materials |
---|---|
MOQ: | 60boxes |
Type: | Silicone Sealant |
State: | Fluid |
Mildew Proof: | Mildew Proof |
Bonding Material: | Glass |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
TEST ITEMS | TEST RESULT | TECHNICAL DATA | STANDARD |
Uncured-Test Conditions: T: (23±2)°C, (50±5)% R.H. | |||
Staining and color change | No staining and no colour change | The sealant shall not cause any visible staining on the top surface of a white cement mortar base | ASTM C510 |
Rheological (Flow) Properties | Vertical displacement: 0 mm sag Horizontal displacement: No deformation |
Vertical displacement: sag W4.8 Horizontal displacement: No deformation |
ASTM C639 |
Extrudability, ml/min | 84 | N10 | ASTM C1183 |
Tack-free Time, h Curing Time, d |
2.5 7~14 |
W3 / |
ASTM C679 |
Range of Application Temperature, °C | 5~40 | / | / |
After cured-Test Conditions: 28 days placed at T: (23±2)P, (50±5)% R.H. | |||
Hardness, Shore A | 38 | Not < 15or >50 | ASTM C661 |
Movement capability % | ±50 | ±50 | ASTM C719 |
Range of Temperature Resistance, °C | -60~180°C | / | / |
Adhesion & Cohesion Under Cyclic Movement | No loss in bond | W9cm2 | ASTM C719 |
Effects of Accelerated Weathering |
No cracks after UV exposure and bend test | Shall no cracks after specified UV & cold temperature exposure and bend test |
ASTM C793 |
Adhesion-In-Peel Average | 76.9 N (17.3 Ibf) cohesive failure within the sealant and no adhesion bond loss between sealant and surface | The peel strength shall N22.2 (5lbf) and the sealant shall show <25% bond loss | ASTM C794 |
Tensile Strength, Mpa | 1.1 | / | ASTM C1135 |
Suppliers with verified business licenses